Effect of endodontic sealers on push-out bond strength of CAD-CAM or prefabricated fiber glass posts

Abstract This study aimed to evaluate the effect of endodontic sealer (ES) on bond strength (BS) of prefabricated or milled-CAD-CAM (computer-aided design and computer-aided manufacturing) glass-fiber-posts (GFP). Canals of 90 single-rooted teeth were prepared for filling by the single-cone technique with gutta-percha and one of the following ES: AH Plus (epoxy resin), Endofill (zinc-oxide and eugenol), and Bio-C Sealer (calcium-silicate). After post-space preparation, tooth-specimens were equally divided in half according to type of GFP to be used. In the half to receive milled-CAD-CAM posts, tooth specimens were molded with acrylic resin to obtain replicas. These were scanned to enable the laboratory to produce the milled-CAD-CAM GFPs (Fiber CAD Lab, Angelus) by the subtractive technique. The other half of samples received prefabricated GFPs (Exacto, Angelus) (n=15). The GFPs were cemented with dual-cure resin cement (Panavia F2.0, Kuraray). Each root was sectioned into two slices per root region (cervical, middle, apical) that were subjected to the push-out BS test, in a universal testing machine. Failure mode (FM) was classified by scores. The BS data were submitted to generalized linear model analyses, while FM was analyzed using the chi-square test (a=0.05). BS showed no significant difference among the three ES (p > 0.05). BS was significantly higher for prefabricated (mean 10.84 MPa) versus milled-CAD-CAM GFPs (mean 6.94 MPa) (p <0.0001), irrespective of ES. The majority showed mixed failures. It could be concluded that type of ES did not affect BS of GFPs to dentin, and prefabricated-GFPs had higher bond-strength than customized-milled-CAD-CAM GFPs.

Influence of restorative materials on occlusal and internal adaptation of CAD-CAM inlays

Aim: To evaluate the occlusal and internal marginal adaptation of inlay restorations made of different materials, using CAD-CAM. Methods: Preparations were made for MOD inlays of one-third intercuspal width and 4 mm depth in 30 third human molars. The teeth were restored using CAD-CAM materials (n=10) of nanoceramic resin (Lava Ultimate), polymer-infiltrated ceramic network (VITA ENAMIC), or lithium disilicate glass-ceramic (IPS e.max CAD). The specimens were cemented with dual resin cement and sectioned at the center of the restoration, after which the two halves were evaluated, and photographed The occlusal and internal discrepancy (µm) was determined at five points: cavosurface angle of the occlusal-facial wall (CA-O); center of the facial wall (FW); faciopulpal angle (FPA); center of the pulpal wall (PW); and center of the lingual wall (LW). The data were submitted to the Kruskal-Wallis and the Dunn tests (α=0.05). Results: No difference was observed among the materials regarding the occlusal discrepancy at the CA-O, FPA, or PW internal points. The e.max CAD measurement at FW showed larger internal discrepancy than that of Lava (p=0.02). The internal discrepancy at LW was greater for e.max CAD than VITA ENAMIC (p=0.02). Conclusion: Lithium disilicate glass-ceramic presented greater internal discrepancy in relation to the surrounding walls of the inlay preparations

Effect of acid challenge and photoactivation distance on microhardness and roughness of flow bulk-fill composite resins / Efeito do desafio ácido e distância de fotoativação na microdureza e rugosidade de resinas compostas bulk-fill flow

Abstract Introduction composite resins are indicated to the reconstruction of proximal walls and the evaluation of properties of flow bulk-fill composite resins exposed to acid challenge is necessary. Objective to evaluate the microhardness and roughness at different depths of photoactivation of bulk-fill flow composites (Filtek Bulk Fill Flow; SureFil SDR Flow; Tetric N Ceram Bulk fill) and conventional composite resin (control, Filtek Z350 XT) subjected to acid challenge. Material and method forty composites brick shaped specimens (3x3x4 mm) were made using a polyacetal matrix. To simulate pH challenges, the samples were immersed in a demineralizing solution. Each sample had Knoop microhardness (KHN) and roughness (Ra) evaluated at three depths (superficial, medium, and cervical), considering the lateral surface of the sample. Data were submitted to Kruskal-Wallis, Friedman's and Dunn's tests with a significance level of 5%. Result comparing the composites among themselves, in superficial (p=0.693), medium (p=0.053) and cervical (p=0.176) regions, there was no difference in the KHN values. There were also no differences in roughness between the composites in superficial (p=0.356), medium (p=0.734) and cervical (p=0.207) regions. Only the Filtek Z350 XT (p=0.027) showed less difference in KHN in the middle region caused by acid challenge. Changes in roughness showed that the greatest difference was at the cervical region for Bulk Fill Flow SDR (p=0.014) and Tetric N-Ceram Bulk Fill (p = 0.003) with an increase after acid challenge. Conclusion after acid challenge, bulk-fill flow composites showed alterations similar to those presented by the conventional nanoparticulate resin composite.

Resumo Introdução as resinas compostas são indicadas para reconstrução de paredes proximais e a avaliação das propriedades das resinas compostas bulk-fill flow expostas ao desafio ácido mostra-se necessária. Objetivo avaliar a microdureza e rugosidade em diferentes profundidades de fotoativação de resinas compostas bulk-fill flow (Filtek Bulk Fill Flow; SureFil SDR Flow; Tetric N Ceram Bulk fill) e convencional (controle, Filtek Z350 XT) submetidas ao desafio ácido. Material e método quarenta amostras retangulares (3x3x4 mm) foram confeccionadas utilizando uma matriz de poliacetal. Para simular o desafio ácido, as amostras foram imersas em uma solução desmineralizante. Cada amostra teve a microdureza Knoop (KHN) e rugosidade (Ra) avaliadas em três profundidades (superficial, média e cervical), considerando a superfície lateral da amostra. Os dados foram submetidos aos testes de Kruskal-Wallis, Friedman e Dunn com nível de significância de 5%. Resultado comparando as resinas compostas entre si, nas regiões superficial (p=0,693), média (p=0,053) e cervical (p=0,176), não houve diferença nos valores de KHN. Também não houve diferenças na rugosidade entre os materiais nas regiões superficial (p=0,356), média (p=0,734) e cervical (p=0,207). Apenas o Filtek Z350 XT (p=0,027) apresentou menor diferença de KHN na região intermediária causada pelo desafio ácido. As mudanças na rugosidade mostraram que a maior diferença foi na região cervical para Bulk Fill Flow SDR (p=0,014) e Tetric N-Ceram Bulk Fill (p=0,003), com aumento após o desafio ácido. Conclusão após desafio ácido, as resinas compostas bulk-fill flow apresentaram alterações semelhantes às apresentadas pela resina composta convencional nanoparticulada.

Influence of calcium lactate and sodium fluoride solution mouthwashes on enamel microhardness and dentin permeability during in-office bleaching / Influência das soluções enxaguatórias de lactato de cálcio e fluoreto de sódio na microdureza do esmalte e permeabilidade dentinária durante o clareamento em consultório

Objective: This study evaluated the influence of calcium lactate and sodium fluoride mouthwashes on enamel microhardness and dentin permeability during in-office bleaching. Material and Methods: For the microhardness evaluation, enamel blocks were randomly submitted to different treatments associated with in-office bleaching agent using 40% hydrogen peroxide (Opalescence Boost PF 40%/ Ultradent; 3 sessions x 40-minute each) (n = 10): 1) Control: application of bleaching agent; 2) Calcium lactate: 1-minute immersion before bleaching treatment; 3) Sodium fluoride: immersion for 1 minute before bleaching treatment; 4) Calcium lactate + sodium fluoride: 1 minute immersion in calcium lactate solution, followed by 1 minute immersion in sodium fluoride before bleaching treatment. Dentin discs received the same treatment protocols (n = 10) to evaluate permeability. Knoop microhardness and dentin permeability assessments were performed twice (at baseline and 48 hours after the end of bleaching treatment). Results: The generalized linear model considering the design of repeated measures over time showed that there was no significant difference between treatments (p = 0.9577) and between assessments (p = 0.3267) regarding Knoop microhardness. Kruskal Wallis and Dunn tests showed that calcium lactate immersion before bleaching treatment provided higher dentin permeability than other groups (p = 0.0009). Conclusion: The use of sodium fluoride solution and calcium lactate in association with in-office bleaching treatment did not influence the microhardness of tooth enamel, although calcium lactate may increase dentin permeability. (AU)

Objetivo: Este estudo avaliou a influência dos enxaguatórios bucais com lactato de cálcio e fluoreto de sódio na microdureza do esmalte e na permeabilidade da dentina durante o clareamento em consultório. Material e Métodos: Para avaliação da microdureza, blocos de esmalte foram submetidos aleatoriamente a diferentes tratamentos associados a agente clareador em consultório com peróxido de hidrogênio 40% (Opalescence Boost PF 40% / Ultradent; 3 sessões x 40 minutos cada) (n = 10): 1) Controle: aplicação de agente clareador; 2) Lactato de cálcio: imersão de 1 minuto antes do tratamento clareador; 3) Fluoreto de sódio: imersão por 1 minuto antes do tratamento clareador; 4) Lactato de cálcio + fluoreto de sódio: 1 minuto de imersão em solução de lactato de cálcio, seguido de 1 minuto de imersão em fluoreto de sódio antes do tratamento clareador. Os discos de dentina receberam os mesmos protocolos de tratamento (n = 10) para avaliar a permeabilidade. As avaliações da microdureza Knoop e da permeabilidade dentinária foram realizadas duas vezes (no início do estudo e 48 horas após o término do tratamento clareador). Resultados: O modelo linear generalizado considerando o delineamento de medidas repetidas ao longo do tempo mostrou que não houve diferença significativa entre os tratamentos (p = 0,9577) e entre as avaliações (p = 0,3267) em relação à microdureza Knoop. Os testes de Kruskal Wallis e Dunn mostraram que a imersão de lactato de cálcio antes do tratamento clareador proporcionou maior permeabilidade dentinária do que os outros grupos (p = 0,0009). Conclusão: O uso de fluoreto de sódio e lactato de cálcio associado ao clareamento em consultório não influenciou a microdureza do esmalte dentário, embora o lactato de cálcio possa aumentar a permeabilidade dentinária (AU)

Diagnostic methods for stained pits and fissures caries lesions on the occlusal surface / Métodos diagnósticos para lesões de cárie com sulcos pigmentados em superfície oclusal

ABSTRACT Objective: The aim of this study was to compare methods for in vitro diagnosis of pigmented pits and fissures on the occlusal surface. Methods: Forty-one human molars and premolars extracted with pigmentation in pits and fissures were used. The teeth were evaluated with artificial illumination for classification according to ICDAS, followed by fluorescent laser evaluation. For the radiographic evaluation, the teeth were positioned to obtain interproximal images, adopting the criterion of Rodrigues et al. 2008 for diagnosis of lesions. For histological evaluation, the teeth were sectioned in the mesiodistal direction in the occlusal sulcus region and evaluated in a 20-fold stereoscopic magnifying glass, using the criterion of Ekstrand et al. (1997) for evaluation. The methods were compared with the histological evaluation, obtaining values of accuracy, sensitivity and specificity regarding the response variables "presence / absence" of enamel caries. Results: When comparing visual inspection with histological analysis, 65.85% accuracy, 40% sensitivity and 90.48% specificity were observed with false positive and negative probability of 20% and 38.71%. When comparing the fluorescent laser with the histological analysis, the accuracy was 58.54%, sensitivity 70% and specificity 47.62%. Comparing the radiographic analysis with the histological analysis, it was obtained 53.66% accuracy, sensitivity of 42.11% and specificity of 73.68%. Conclusion: The ROC curve and the Yuden index showed that visual inspection presented the best combination of sensitivity and specificity than fluorescent laser and radiographic analysis for diagnosis, which represented the best method for detecting inactive carious lesions in enamel.

RESUMO Objetivo: O objetivo deste estudo foi comparar métodos para diagnóstico in vitro de sulcos pigmentados em superfície oclusal. Métodos: Foram utilizados 41 molares e pré-molares humanos extraídos com pigmentação em sulcos e fissuras. Os dentes foram avaliados com iluminação artificial para classificação quanto ao critério ICDAS, seguida por avaliação com laser fluorescente. Para a avaliação radiográfica, os dentes foram posicionados para obtenção de imagens interproximais, adotando-se o critério de Rodrigues et al. (2008) para diagnóstico. Para avaliação histológica, os dentes foram seccionados no sentido mésio-distal na região de sulco oclusal e avaliados em lupa estereoscópica com aumento de 20 vezes, adotando-se o critério de Ekstrand et al. (1997). Os métodos foram comparados com a avaliação histológica, obtendo-se valores de acurácia, sensibilidade e especificidade quanto às variáveis de resposta "presença/ausência" de lesão de cárie em esmalte. Resultados: Ao comparar a inspeção visual com a análise histológica, observou-se acurácia de 65,85%, sensibilidade de 40% e especificidade de 90,48%. Ao comparar o laser fluorescente com a análise histológica, a acurácia foi de 58,54%, sensibilidade de 70% e especificidade de 47,62%. Na comparação da análise radiográfica com a histológica, obteve-se acurácia de 53,66%, sensibilidade de 42,11% e especificidade de 73,68%. Conclusão: A curva ROC mostrou que a inspeção visual apresentou a melhor combinação de sensibilidade e especificidade que o laser fluorescente e que a análise radiográfica para o diagnóstico, representando o melhor método para detecção de cárie em lesões com sulcos pigmentados em esmalte

Effect of different concentrations of green tea extract solutions on bonding durability of etchand- rinse adhesive system to caries affected dentin

Aim: The in vitro study evaluated the effect of different concentrations of green tea extract solution (GT) on the bonding durability of etch-and-rinse adhesive system to caries dentin affected (CAD). Methods: Dentinal surfaces of human third molars were polished and submitted to a microbiological caries induction protocol for 14 days. After removal of the infected dentin layer, the samples were randomly divided into 4 groups (n= 10), according to the concentration of GT solution applied in CAD, after acid etching: 0.05%; 0.2%; 2% and NT (no treatment ­ control). After application of a etch-and-rinse adhesive system (Adper Single Bond 2, 3M ESPE), composite resin restorations were performed on the dentin. After 24 hours, the resin-dentin blocks were sectioned 1mm2 specimens, which were subjected to the microtensile test immediately or after 6 months of storage in water. Data were submitted to two-way ANOVA for randomized blocks and Tukey test (α= 5%). Results: There was no effect of double interaction (p= 0.934). The application of 0.2% GT promoted a statistically significant increase in dentin bond strength values in comparison to the condition where GT was not used (p=0.012). There was a significant decrease of bond strength after 6 months of storage, regardless of dentin pretreatment (p = 0.007). The G test identified that there was no statistical difference regarding failure mode (p= 0.326). Conclusion: The concentration of 0.2% improved the bond strength of an etch-and-rinse adhesive system to caries affected dentin, however, none of dentin pretreatments could prevent the decrease in bond strength over time

Effect antioxidants application on microshear bond strength of universal adhesive to bleached enamel / Efeito da aplicação de antioxidantes na resistência de união do adesivo universal ao esmalte clareado

Purpose: To evaluate, in vitro, the influence of antioxidants (green tea extract - GT and sodium ascorbate - SA) on microshear bond strength (µSBS) of a universal adhesive system ­ self-etching mode (UAS) to bleached enamel. Material and Methods: After obtaining 50 fragments of human dental enamel (4 mm x 4 mm), forty fragments were submitted to at-home bleaching technique using 10% carbamide peroxide (Opalescence PF, Ultradent) for two h/day, for four weeks. They were randomly divided in four groups (n = 10): GT - 10% aqueous GT solution (60 min); SA - 10% SA solution (10 min); Negative control - no antioxidant agent, immediately restored; PC1 (positive control 1) - no antioxidant agent, restored 14 days the bleaching procedure. Ten enamel fragments were assigned to PC2 group (positive control 2), in which the adhesive procedures were realized in non-bleached enamel. The UAS (Adper Single Bond Universal, 3M ESPE) was applied on enamel surface according to manufacturer's instructions and two cylinders (0.8 mm diameter) of nanoparticulate composite resin (Z350, 3M ESPE) were made on each sample. After 24 h, the cylinders were submitted to µSBS in a universal test machine (0.5 mm/min). Fracture mode was evaluated in stereomicroscope (30x magnification). SBS data, in MPa, was submitted to one-way ANOVA and fracture mode to Chi-square test (α = 0.05). Results: There was no statistical difference between the experimental groups (p = 0.545) and fracture mode (p = 0.16424). There was predominance of adhesive fracture in all groups. Conclusion: Neither the bleaching procedure nor the application of antioxidants to bleached enamel interfered in the bond strength of the tested universal adhesive system (AU)

Objetivo: Avaliar, in vitro, a influência de antioxidantes (extrato de chá verde - GT e ascorbato de sódio - SA) na resistência de união ao microcisalhamento (µSBS) de um sistema adesivo universal - modo de autocondicionamento (UAS) ao esmalte clareado. Material e Métodos: Realizou-se a obtenção de 50 fragmentos de esmalte dental humano (4 mm x 4 mm), sendo que desses, quarenta fragmentos foram submetidos à técnica de clareamento caseiro utilizando peróxido de carbamida a 10% (Opalescence PF, Ultradent) por duas horas/dia, durante quatro semanas. Eles foram divididos aleatoriamente em quatro grupos (n= 10): Expostos a GT - solução aquosa de GT a 10% (60 min); expostos a SA - solução 10% SA (10 minutos); Sem exposição ao agente antioxidante e imediatamente restaurado - (controle negativo); Sem exposição ao agente antioxidante e restaurado 14 dias após o clareamento - PC1 (controle positivo 1). Os dez fragmentos de esmalte restantes foram atribuídos ao grupo PC2 (controle positivo 2), no qual os procedimentos adesivos foram realizados em esmalte não clareado. O UAS (Adper Single Bond Universal, 3M ESPE) foi aplicado na superfície do esmalte de acordo com as instruções do fabricante e dois cilindros (0,8 mm de diâmetro) de resina composta nanoparticulada (Z350, 3M ESPE) foram feitos em cada amostra. Após 24 h, os cilindros foram submetidos ao µSBS em uma máquina de teste universal (0,5 mm/min). O modulo de fratura foi avaliado em estereomicroscópio (aumento de 30x). Os dados do SBS, em MPa, foram submetidos à ANOVA unidirecional e ao modo fratura ao teste do qui-quadrado (α = 0,05). Resultados: Não houve diferença estatística entre os grupos experimentais (p = 0,545) e modulo de fratura (p = 0,16424). Houve predomínio de fratura adesiva em todos os grupos. Conclusão: Nem o procedimento de clareamento nem a aplicação de antioxidantes no esmalte clareado interferiram na resistência de união do sistema adesivo universal testado. (AU)

Color stability of a bulk-fill composite resin light-cured at different distances

Abstract The aim of this in vitro study was to evaluate the color stability of a bulk-fill (Filtek One Bulk Fill, 3M ESPE) and a conventional (Filtek Z350 XT, 3M ESPE) composite resin light-cured at different distances, before and after being submitted to staining with a coffee solution. Sixty specimens of each composite resin were prepared and light-cured at distances of 0, 2 and 4 mm, using a LED light-curing unit (Valo, Ultradent). The specimens were separated (n = 10) for immersion in either distilled water or coffee solution (10 minutes a day for 8 days) to stimulate staining. Color evaluations were performed before and after immersion in the solutions, according to CIELab (△Eab), CIEDE2000 (△E00) and the Whiteness Index for Dentistry (△WID). Kruskal Wallis and Dunn tests, Mann-Whitney tests and Wilcoxon test were applied (α = 5 %). The a* value for conventional composite resin showed a significant increase after immersion in coffee and distilled water (p < 0.05). Both composite resins showed greater b* values when immersed in coffee than in distilled water, with no significant difference among the light-activation distances (p > 0.05). There was no significant difference for L* among the light-activation distances; both resins showed significant decrease in L* after immersion in coffee (p < 0.05). Color change (△Eab, △E00) and difference in whiteness (△WID) were higher for conventional resin when immersed in the coffee solution at all the light-activation distances. Conventional composite resin presented a higher staining value than bulk-fill composite resin, regardless of the light-activation distance.

Hardness, compressive strength and resilience of complete denture lining materials: an in situ study / Dureza, resistência à compressão e resiliência de materiais de reembasamento para próteses totais: estudo in situ

ABSTRACT Objective The aim of this study was to evaluate the in situ hardness, compressive strength and resilience of soft lining materials used in total removable prostheses in different time intervals Methods total of 48 rectangular test specimens (10 x 3 x 2 mm) were fabricated of each of the polyvinylsiloxane-based soft liner (Mucopren Soft) and acrylic resin-based material (Trusoft), which were placed on total removable prostheses bases of 12 volunteers (n = 12). The hardness (Shore A), compressive strength (in MPa) and resilience (in Kgf/cm2) were evaluated in different time intervals: 0, 7, 30 and 60 days, at three different locations of the specimens surface. Results The two-way ANOVA and Tukey test showed that the polyvinylsiloxane-based soft liner presented higher hardness values (p = 0.0113) and higher compressive strength (p=0.0252) than the acrylic resin-based material at immediate and 7 days evaluations. The polyvinylsiloxane-based soft liner presented higher resilience values than the acrylic resin-based material at all times (p = 0.0133). Hardness and compressive strength were similar for both materials at 30 and 60 days evaluations. Conclusions For both materials,there was a tendency for an increase of hardness, compressive strength and resilience over time, influenced by the composition of the tissue conditioner. The polyvinylsiloxane-based soft liner presented higher hardness, compressive strength and resilience than the acrylic resin-based material, specially considering a long-term evaluation up to 60 days.

RESUMO Objetivo O objetivo deste estudo foi avaliar in situ a dureza, resistência à compressão e resiliência de materiais para reembasamento utilizadas em próteses totais removíveis em diferentes intervalos de tempo. Métodos Um total de 48 corpos de prova retangulares (10 x 3 x 2 mm) foram confeccionados de cada uma dos reembasadores a base de polivinilsiloxano (Mucopren Soft, Kettenbach GmbH & Co) e resina acrílica (Trusoft, Bosworth), os quais foram posicionados na base de próteses totais removíveis de 12 voluntários (n = 12). A dureza (Shore A), resistência à compressão (em MPa) e resiliência (em Kgf/cm2) foram avaliadas em diferentes intervalos de tempo: 0, 7, 30 e 60 dias, em três diferentes localizações da superfície do corpo de prova. Resultados A ANOVA a dois critérios e o teste de Tukey mostraram que o reembasador a base de polivinilsiloxano apresentou maiores valores de dureza (p = 0,0113) e maior resistência à compressão (p=0,0252) do que o a base de resina acrílica nas avaliações nos tempos imediato e 7 dias. O reembasador a base de polivinilsiloxano apresentou maior resiliência que o a base de resina acrílica em todos os tempos (p = 0,0133). Dureza e resistência à compressão foram semelhantes para ambos os materiais nos tempos 30 e 60 dias de avaliação. Conclusões Para ambos os materiais, houve tendência de aumento da dureza, resistência à compressão e resiliência com o passar do tempo, influenciado pela composição dos materiais de rembasamento tecidual. O reembasador a base de polivinilsiloxano apresentou maior dureza, resistência à compressão e resiliência que o a base de resina acrílica, considerando-se especialmente o tempo de avaliação de 60 dias.

Titanium dioxide nanotubes incorporated into bleaching agents: physicochemical characterization and enamel color change

Abstract Titanium dioxide nanotubes are nanostructures that can accelerate the oxidation reaction of bleaching procedures and promote a more effective whitening effect. Objective This study evaluated physicochemical properties of bleaching agents incorporated with titanium dioxide (TiO2) nanotubes, and the effects on tooth color change at different periods. Methodology 40 premolars were treated according to the following groups (n=10): CP - 10% carbamide peroxide (1 hour daily/21 days); CPN - CP incorporated into TiO2; HP - 40% hydrogen peroxide (three 40-minute sessions/7 days apart); HPN - HP incorporated into TiO2. Color shade was evaluated at five different periods (baseline, after 7, 14 and 21 days of bleaching, and 7 days after end of treatment) according to Vita Classical, CIELab and CIEDE2000 scales. Mean particle size (P), polydispersity (PO) and zeta potential (ZP) were evaluated using dynamic light scattering. Data on the different variables were analyzed by mixed model tests for measures repeated in time (ZP e L*), generalized linear models for measures repeated in time (P, PO, Vita Classical and b*), and Friedman and Mann-Whitney tests (a* and color change/ΔE and ΔE00). Results CP and CPN presented higher P, higher PO and lower ZP than HP and HPN (p≤0.05). All groups showed a significant decrease in Vita Classical color scores after 7 days of bleaching (p<0.05), and HPN presented a greater significant reduction than the other groups. L* increased in TiO2 presence, in all groups, without any differences (p>0.05) in bleaching time. A significant reduction occurred in the a* and b* values for all the groups, and HPN presented lower a* and b* values (p<0.05) than CPN. ΔE was clinically noticeable after 7 days, in all groups, and all groups resulted in a perceptible color change according to ΔE00. Conclusion TiO2 did not influence physicochemical properties of the bleaching agents. HPN presented more effective tooth bleaching than CPN.

Mechanical and histological evaluation of a titanium device for orthodontic anchorage, placed with or without cyanoacrylate adhesive

ABSTRACT Objective: The objective of the present study was to perform a histological evaluation of a titanium mini-implant for orthodontic anchorage. Shear strength and fracture patterns that occurred immediately, 30 and 60 days after insertion with or without N-2-butyl-cyanoacrylate adhesive were evaluated. Methods: Ninety-six mini-implants (Arrow, Peclab, Brazil) were placed in the tibia of 9 male rabbits, with or without an adhesive (Vetbond™, 3M, USA). Histological evaluation was done by optical light microscope. Shear strength testing was performed, followed by fracture analysis with visual inspection. Results: Close contact between the newly formed bone and the device was evidenced in the group without adhesive, whereas gaps in the group with adhesive were found. Tukey test showed similar values in both groups at the immediate time point (20.70 N without adhesive and 24.69 N with adhesive), and higher values for the non-adhesive group, after 30 and 60 days (43.98 N and 78.55 N, respectively). The values for the adhesive group were similar for the immediate time point (24.69 N), 30 days (18.23 N) and 60 days (31.98 N). The fractures were adhesive for both groups at the immediate time point. The fractures were cohesive in bone for the non-adhesive group after 30 and 60 days. Conclusions: The mini-implants showed close bone contact and required higher shear strength for removal at 30 and 60 days for the non-adhesive group. Further studies are needed to assess the proper way to remove the orthodontic anchorage without cohesive fractures in bone.

RESUMO Objetivos: este estudo teve como objetivo realizar uma avaliação histológica de um mini-implante para ancoragem em Ortodontia. Avaliou-se, também, a carga de cisalhamento e o padrão de fratura imediatamente e após 30 e 60 dias da sua inserção, com ou sem o uso do adesivo N-butil-2-cianoacrilato. Métodos: noventa e seis mini-implantes (Arrow, Peclab, Brasil) foram instalados na tíbia de nove coelhos machos, com ou sem adesivo (Vetbond™, 3M, EUA). A avaliação histológica foi realizada com uso de microscópico de luz óptica. Realizou-se o teste de resistência ao cisalhamento, seguido pela análise da fratura, por meio de inspeção visual. Resultados: um contato íntimo entre o novo osso formado e o dispositivo foi evidenciado no grupo sem adesivo, enquanto espaços foram encontrados no grupo com adesivo. O teste de Tukey mostrou valores semelhantes em ambos os grupos no tempo imediato (20,70 N sem adesivo e 24,69 N com adesivo), e valores maiores para o grupo sem adesivo após 30 e 60 dias (43,98 N e 78,55 N, respectivamente). Os valores para o grupo com adesivo foram semelhantes para os tempos imediato (24,69 N), 30 dias (18,23 N) e 60 dias (31,98 N). As fraturas foram adesivas para ambos os grupos, no tempo imediato. As fraturas foram coesivas no osso para os grupos sem adesivo, após 30 e 60 dias. Conclusões: os mini-implantes mostraram um contato íntimo com o osso e requereram alta carga de cisalhamento para sua remoção após 30 e 60 dias nos grupos sem adesivo. Estudos adicionais são necessários para avaliar um método para remoção do dispositivo ortodôntico sem fratura coesiva no osso.

Remineralizing effect of commercial fluoride varnishes on artificial enamel lesions

Abstract: The aim of this study was to evaluate soluble and insoluble fluoride concentrations in commercial varnishes, and their remineralization effect on artificial caries enamel lesions using surface and cross-sectional microhardness evaluations. Forty bovine enamel blocks were separated into four groups (n=10): control (no treatment), Enamelast (Ultradent Products), Duraphat (Colgate-Palmolive) and Clinpro White Varnish (3M ESPE). Surface enamel microhardness evaluations were obtained, artificial enamel caries lesions were developed by dynamic pH-cycling, and the varnishes were then applied every 6 days, after which the enamel blocks were submitted to dynamic remineralization by pH cycles. After removal of the varnishes, the enamel surfaces were reassessed for microhardness. The blocks were sectioned longitudinally, and cross-sectional microhardness measurements were performed at different surface depths (up to 300 μm depth). Polarized light microscopy images (PLMI) were made to analyze subsurface caries lesions. The fluoride concentration in whole (soluble and insoluble fluoride) and centrifuged (soluble fluoride) varnishes was determined using an extraction method with acetone. The data were analyzed to evaluate the surface microhardness, making adjustments for generalized linear models. There was a significant decrease in enamel surface microhardness after performing all the treatments (p<0.0001). Enamelast and Duraphat showed significantly higher enamel microhardness values than the control and the Clinpro groups (p = 0.0002). Microhardness loss percentage was significantly lower for Enamelast (p = 0.071; One-way ANOVA). PLMI showed that subsurface caries lesions were not remineralized with the varnish treatments. No significant differences in the in-depth microhardness levels (p = 0.7536; ANOVA) were observed among the treatments. Enamelast presented higher soluble and insoluble fluoride concentrations than the other varnishes (p < 0.0001; Kruskal-Wallis and Dunn tests). Enamelast and Duraphat varnishes promoted enamel surface remineralization, but no varnish remineralized the subsurface lesion body. Although insoluble and soluble fluoride concentration values did not correspond to those declared by the manufacturer, Enamelast presented higher fluoride concentration than the others.

Sour Gummy Candies and their Effect on Salivary pH kinetics

Objective: This randomized controlled crossover clinical trial monitored the kinetics of salivary pH over time following the consumption of sour gummy candy. Material and Methods: Twenty participants underwent saliva assessment for flow, pH and buffer capacity. Following a two-arm crossover layout, the participants chewed a piece of a sour and a piece of an ordinary (control) gummy candy for 20 seconds. Participants expectorated saliva at 18 time points: immediately after ingesting the candies; then after every 15 second interval, for up to 1 minute; 30 seconds up to 4 minutes; 60 seconds up to 10 minutes; and at 15 minutes. The pH of the collected samples was measured with a pH microelectrode. The data concerning the pH measurements of the whole saliva samples collected over time following chewing of sour and ordinary gummy candies underwent repeated-measures three-way analysis of variance (ANOVA) using a significance level of 5%. Results: Repeated-measures three-way analysis of variance demonstrated a significant interaction between the type of candy and time (p<0.001). Tukey's test revealed that with the consumption of sour gummy candy, the salivary pH showed an initial marked exponential drop and remained lower than that observed with the consumption of the ordinary version for up to 120 seconds. Conclusion: The consumption of sour gummy candy induces a major, transient fall in salivary pH, which may represent a risk factor for dental erosion.

Whitening mouthwash containing hydrogen peroxide decreases enamel microhardness in vitro

Aim: To assess the effect of a mouthwash containing hydrogen peroxide (HP) on Knoop microhardness (KMH) of bovine enamel. Methods: Fifty-one enamel slabs were polished and divided into groups (n=17), according to the product used during 28 days: HP ­ mouthwash containing 1,5% of HP (4 min, once/day); CP - 10% carbamide peroxide gel (2 hours/day); AS - no treatment (kept in artificial saliva (AS). Each fragment was submitted to KMH test (three indentations/fragment, with a 50 g load for 5 sec) four times: before (baseline); during (14 and 28 days) and after (7 days immerged in AS) the bleaching treatment. The data were submitted to repeated-measures two-way ANOVA (α=0.05). Results: There was no effect of the interaction between the time and treatment factors (p=0.327). No significant effect was observed from the time factor (p = 0.054). The factor treatment showed significant effect (p =0.002). Regardless of time, the KMH of the enamel submitted to HP was lower than the value observed with the use of CP, which did not differ significantly from the control group (AS). Conclusion: Although there was a trend of decreasing enamel microhardness over time, only the mouthwash containing hydrogen peroxide had a significant effect (AU)

Evaluation of the anti-cariogenic potential and bond strength to enamel of different fluoridated materials used for bracket bonding / Avaliação do potencial anti-cariogênico e da resistência adesiva ao esmalte de diferentes materiais contendo fluoreto, utilizados para colagem de braquetes

Objective: To evaluate the in vitro and in situ anti-cariogenic potential and bond strength to enamel of materials containing fluoride (F), used for bracket bonding: Transbond XT (GT, negative control), Transbond Plus Color Change (GTF), Transbond-Self-Etching Primer (GSAF) and Vitremer (GV, positive control). Material and method: In the in vitro study, the specimens were premolars with bonded brackets (n=12/group). After pH cycling, the F release, bond strength, fracture mode and presence of white spot lesions were assessed. In the in situ study, the specimens were enamel fragments with bonded brackets (n=12/group). Twelve volunteers wore palatal appliances in 4 phases, with cariogenic challenge. Bond strength, fracture mode and change in surface hardness (%SH) were determined. Result: Relative to the in vitro study, F release (ppm) was: GT=0.257±0.068c; GTF=0.634±0.100b; GSAF=0.630±0.067b; GV=2.796±1.414a. Only GV showed no white spot lesions. Bond strength values (MPa) were GT=7.62±7.18a; GTF=5.15±6.91ab; GSAF=3.42±2.97bc; GV=2.87±2.09c. Adhesive fracture was the most frequent type, except for GTF. In the in situ study, %SH was: GT=-56.0±18.3a; GTF=-57.6±11.9a; GSAF=-57.1±11.3a; GV=-52.4±25.8a. Bond strength values were GT=9.5±4.4a; GTF=11.1±5.9a; GSAF=13.2± 6.6a; GV=6.6±4.0a. Cohesive fracture in material was the most frequent type, except for GTF. Conclusion: Vitremer (GV) showed the highest anti-cariogenic potential in the in vitro study. However, it was not confirmed by the in situ study. Regarding bond strength values from the in situ study, all materials were shown to be adequate for clinical practice.

Objetivo: Avaliar in vitro e in situ o potencial anti-cariogênico e a resistência adesiva ao esmalte de materiais contendo fluoreto utilizados para a colagem de braquetes: Transbond XT (GT, controle negativo), Transbond Plus Color Change (GTF), Transbond Self Etching Primer (GSAF) and Vitremer (GV, controle positivo). Material e método: No estudo in vitro, as unidades experimentais foram premolares com braquetes colados (n = 12/grupo). Após ciclagem de pH, a liberação de F, resistência adesiva, modo de fratura e presença de mancha branca foram avaliados. No estudo in situ, as unidades experimentais foram fragmentos de esmalte com braquetes colados (n = 12/grupo). Os doze voluntários utilizaram dispositivos palatinos em 4 fases, com desafio cariogênico. Resistência adesiva, modo de fratura e variação de dureza superficial (%SH) foram determinados. Resultado: No estudo in vitro, a libertação de F (ppm) foi: GT=0,257±0,068c; GTF=0,634±0,100b; GSAF=0,630±0,067b; GV=2,796±1,414a. Apenas GV não apresentou lesões de mancha branca. Os valores de resistência de união (MPa) foram GT=7,62±7,18a; GTF=5,15±6,91ab; GSAF=3,42±2,97bc; GV=2,87±2,09c. A fratura adesiva foi mais frequente, com exceção de GTF. Para o estudo in situ, % SH foi: GT=-56,0±18,3a; GTF=-57,6±11,9a; GSAF=-57,1±11,3a; GV=-52,4±25,8a. Os valores de resistência de união foram GT=9,5±4,4a; GTF=11,1±5,9a; GSAF=13,2±6,6a; GV=6,6±4,0a. Fratura coesiva no material foi a mais frequente, exceto para GTF. Conclusão: Vitremer (GV) apresentou maior potencial anti-cariogênico no estudo in vitro, mas isso não se confirmou no estudo in situ. Os valores de resistência de união, a partir do estudo in situ, demonstraram que eles são adequados para a prática clínica.

Long-term bond strength of a self-adhesive resin cement to intraradicular dentin pretreated with chlorhexidine and ethanol / Resistência de união ao longo do tempo de um cimento resinoso autoadesivo à dentina intrarradicular pré tratadas com clorexidina e etanol

Introduction: Self-adhesive resin cements do not require prior preparation of the tooth surface, therefore dentin pretreatments may influence long-term bond strength. Objective: To evaluate the influence of 100% ethanol (ET) and 2% chlorhexidine (CL) treatment of intraradicular dentin on the long-term bond strength (BS) of a self-adhesive resin cement (SRC). Material and method: 80 bovine roots were restored with fiber posts and SRC (U200 3M/ESPE) and distributed into 4 groups according to dentin treatment: Group 1 – without treatment; Group 2 – 2% CL for 1 minute; Group 3 – 100% ET for 1 minute; Group 4 – 2% CL, followed by 100% ET. The samples were cross-sectioned to obtain two sections (0.7 mm) thick for each root third: coronal, middle and apical. The immediate push-out test was carried out after 48 hours, and the long-term push-out test, after 180 days. Result: The three-way ANOVA test for randomized blocks showed no difference between the BS values at 48 hours and 80 days, irrespective of the treatment and the third (p>0.05). The interaction of the treatment/third pairing was significant (p = 0.041) since the treatment with CL promoted lower BS in the coronal third, while treatment with ET promoted better BS in the apical third. Conclusion: Treatment with CL and ET, separately or combined, promoted no differences between the BS values of the SRC to root dentin over time.

Introdução: Cimentos resinosos autoadesivos não necessitam de tratamento prévio da superfície dental, por esta razão o pré tratamento da dentina pode influenciar a longevidade da resistência adesiva. Objetivo: Avaliar a influência do tratamento dentinário com etanol (ET) 100% e clorexidina (CL) 2% na resistência de união (RU) de um cimento resinoso autoadesivo (CRA) à dentina intrarradicular. Material e método: 80 raízes bovinas restauradas com pino de fibra de vidro e CRA (U200 3M/ESPE) foram distribuídas em 4 grupos, de acordo com o tratamento prévio da dentina intrarradicular: Grupo 1 – nenhum tratamento; Grupo 2 – CL2% por 1 minuto; Grupo 3 – ET100% por 1 minuto; Grupo 4 – CL2% seguido pelo ET100%. As amostras foram seccionadas no sentido radial para obtenção de duas secções de aproximadamente 0,7 mm de espessura em cada terço – cervical, médio e apical. Após 48 horas e 180 dias foi realizado o teste push-out. Resultado: A ANOVA a três critérios para blocos casualizados demostrou que não houve diferença entre os valores de resistência de união nos tempos 48 h e 180 dias, independentemente do tratamento e do terço (p>0,05). A interação tratamento-terço foi significativa (p = 0,041) sendo que o tratamento com CL promoveu menor RU no terço cervical e o tratamento com ET promoveu melhor RU no terço apical. Conclusão: Os tratamentos com CL e ET individualmente ou associados não promoveram diferenças entre os valores de RU do CRA à dentina intrarradicular ao longo do tempo.

Chitosan in different concentrations added to a two-step etch-and-rinse adhesive system: influence on bond strength to dentin / Quitosana em diferentes concentrações adicionada a um sistema adesivo convencional de dois passos: influência na resistência de união à dentina

Objectives: the aim of the present study was to evaluate the influence of adding different concentrations of chitosan to an experimental two-step etch-and-rinse adhesive system on the bond strength and failure mode to dentin. Material and Methods: thirty-two flat dentin surfaces were obtained from extracted human third molars and divided into four groups (n=8) for application of the adhesive systems: AD - conventional two-step adhesive system (Adper Single Bond 2); EXP ­ experimental two-step etch-and-rinse adhesive system; Chi0.2% - EXP with addition of 0.2% Chitosan; Chi0.5% - EXP with addition of 0.5% Chitosan. Resin composite build-ups were made and the composite/ dentin specimens were sectioned to obtain rectangular beams with a bond area of approximately 1mm2 . After 24 hours, the sticks were submitted to microtensile bond strength tests in a universal test machine. The fracture pattern was evaluated under a stereoscopic loupe at 40X magnification. Results: one-way analysis of variance showed that the type of adhesive system had no significant effect on the bond strength values (p = 0.142), showing the mean bond strength values (standard deviation), in MPa, for the groups as follows: AD=20.1 (5.4); EXP=16.6 (2.3); Chi0.2%=16.1 (2.8); Chi0.5%=16.9 (2.3). In all the groups there was predominance of cohesive fractures in dentin, representing 68 to 82% of the failure modes. Conclusion: the addition of 0.2 or 0.5% of chitosan had no influence on the bond strength and failure mode of an experimental two-step etch-andrinse adhesive system to dentin. (AU)

Objetivo: o objetivo deste estudo foi avaliar a influência da incorporação de diferentes concentrações de quitosana em um sistema adesivo experimental convencional de dois passos na resistência de união à dentina e modo de falha. Material e Métodos: trinta e duas superfícies de dentina planificadas foram obtidas de terceiros molares e separadas em quatro grupos (n=8) para aplicação dos sistemas adesivos: AD - sistema adesivo convencional de dois passos (Adper Single Bond 2); EXP ­ sistema adesivo convencional de dois passos experimental; Chi0,2% - EXP com incorporação de quitosana a 0,2%; Chi0,5% - EXP com incorporação de quitosana a 0,5%. Blocos de resina composta foram confeccionados e os espécimes de resina composte/ dentina foram seccionados para se obter palitos retangulares com interface adesiva foi seccionada para obtenção de palitos com área de união de aproximadamente 1mm2 . Após 24 horas, os palitos foram submetidos aos testes de resistência de união por microtração em máquina universal de ensaios. O modo de falha foi avaliada em lupa estereoscópica com aumento de 40 vezes. Resultados: análise de variância a um critério mostrou que o tipo de sistema adesivo não apresentou efeito significativo nos valores de resistência de união (p = 0,142), observando-se os respectivos valores de média (desvio-padrão), em MPa, para os grupos: AD=20,1 (5,4); EXP=16,6 (2,3); Chi0,2%=16,1 (2,8); Chi0,5%=16,9 (2,3). Para todos os grupos houve predominância de fraturas coesivas em dentina, representando 68 a 82% dos modos de falhas. Conclusão: a incorporação de quitosana a 0,2 ou 0,5% na influenciou a resistência de união à dentina e o modo de falha de um sistema adesivo convencional de dois passos experimental à dentina. (AU)

Comparative analysis of plastic deformation of NiTi and CuNiTi wires submitted to mechanical cycling / Análise da deformação plástica em fios ortodônticos de NiTi e CuNiTi submetidos à ciclagem mecânica

Objective: O objetivo deste trabalho foi avaliar a deformação plástica em fios NiTi e CuNiTi submetidos à ciclagem mecânica. Material e Métodos: Utilizaram-se fios ortodônticos de CuNITi de cinco marcas comerciais (n=10): RMO, Orthometric, Ormco, Aditek e Eurodonto; e um grupo controle de fio NiTi: Aditek termoativado. Todos os fios, com calibre 0.016'', foram encaixados em slots de quatro bráquetes convencionais alinhados e fixados a uma placa de acrílico. O teste foi realizado com aplicação de carga de 3 N e frequência de 2 Hz entre os dois bráquetes mais centrais, limitando-se à 10.000 ciclos. Após a ciclagem, observou-se a presença ou ausência de fratura dos fios. Não havendo fratura, os fios foram analisados quanto à deformação plástica com uso de transferidor, medindo-se a angulação do fio deformado. Resultados: Os resultados mostraram que não houve fratura de nenhum dos fios analisados. O teste de Kruskal-Wallis mostrou diferenças entre as angulações dos fios ortodônticos (p=0.0009). Com exceção dos fios da Ormco, os demais apresentaram deformação plástica. A maior mediana do valor de angulação foi observada para o fio Aditek Cuper NiTi. Observou-se que as menores medianas foram observadas para os fios RMO, Eurodonto e Ormco. Os fios Aditek termoativado e Orthometric apresentaram angulação intermediária. Conclusão: Nenhum dos fios analisados apresentou fratura. Houve diferenças quanto à deformação plástica sofrida pelos fios avaliados, independentemente da presença de cobre na sua composição química, sendo que o fio Ormco foi o único que não apresentou qualquer deformação. (AU)

Objetivo: The aim of this study was to evaluate the plastic deformation of NiTi and CuNiTi archwires submitted to mechanical cycling. Material and Methods: Orthodontic archwires made of CuNiTi of five commercial brands (n=10) were used: RMO, Orthometric, Ormco, Aditek and Eurodonto; and a Control Group of NiTi archwire: Aditek thermoactivated. All the archwires, with caliber 0.016", were fitted into the slots of four conventional brackets, aligned and fixed to an acrylic plate. The test was performed by applying a load of 3 N and frequency of 2 Hz between the most central brackets, limited to 10,000 cycles. After cycling, the presence or absence of archwire fracture was observed. When there was no fracture, the archwires were analyzed relative to plastic deformation with the use of a transferer, measuring the angulation of the deformed archwire. Results: The results showed that there was no fracture in any of the wires analyzed. The Kruskal-Wallis test showed differences among the angulations of the orthodontic archwires (p=0.0009). With exception of the Ormco wires, the other types presented plastic deformation. The highest median of the angulation value was observed for the Aditek Copper NiTi archwire. The lowest median values were observed for the RMO, Eurodonto and Ormco archwires. The Aditek thermoactivated and Orthometric archwires presented intermediate angulation. Conclusion: None of the archwires analyzed presented fracture. These archwires presented differences in plastic deformation, irrespective of the presence of copper in their chemical composition. The Ormco archwire was the only type that presented no deformation whatever (AU)

Longevity of restorations in direct composite resin: literature review / Longevidade de restaurações diretas em resina composta: revisão de literatura

ABSTRACT Composite resin restorations have increased considerably in popularity and predictability, enabling the realization of a minimally invasive dental treatment. However, to obtain the success of composite resin restorations, knowledge of adhesives and the use of the technique are required, otherwise failure may appear quickly. The objective of the present work was to conduct a literature review on the clinical performance of different types of composite resins and adhesive systems with regard to longevity. For this evaluation, some characteristics of the restorations were immediately verified after they were completed and after a determined time. Characteristics such as postoperative sensitivity, color, marginal integrity, secondary caries, texture, marginal adaptation, retention, displacement, marginal discoloration and anatomical shape had their performances compared. The influence of different adhesive systems on the longevity of the restorations was also observed as a function of its fundamental importance in the union between the tooth and the restorative material. It was concluded that most restorations performed clinically acceptable when hybrid, nanoparticle or microhybrid composite resins and conventional adhesive systems were used.

RESUMO As restaurações de resinas compostas têm aumentado consideravelmente em popularidade e previsibilidade, possibilitando a realização de um tratamento odontológico minimamente invasivo. No entanto, para se obter o sucesso das restaurações de resina composta é necessário ter conhecimento dos materiais adesivos e da técnica de utilização, caso contrário os insucessos podem aparecer rapidamente. Assim, o objetivo deste trabalho foi realizar uma revisão de literatura sobre o desempenho clínico de diferentes tipos de resinas compostas e de sistemas adesivos no que se refere à longevidade. Para essa avaliação foram verificadas algumas características das restaurações logo após elas serem finalizadas e depois de um determinado tempo. Características como sensibilidade pós-operatória, cor, integridade marginal, cárie secundária, textura, adaptação marginal, retenção, deslocamento, descoloração marginal, forma anatômica, tiveram seus desempenhos comparados. A influência dos vários sistemas adesivos na longevidade das restaurações foi também observada em função da sua fundamental importância na união entre o dente e o material restaurador. Concluiu-se que a maioria das restaurações se apresentou clinicamente aceitável, quando se usou resinas compostas híbridas, nanoparticuladas ou microhíbridas e sistema adesivo convencional.

Influence of ligation method on friction resistance of lingual brackets with different second-order angulations: an in vitro study

ABSTRACT Objective: To evaluate stainless steel archwire static friction in active and passive self-ligating lingual and conventional brackets with second-order angulations. Methods: Two conventional lingual brackets for canines (STb light/Ormco; PSWb/Tecnident), and two self-ligating brackets, one active (In-Ovation L/GAC) and the other passive (3D/ Forestadent), were evaluated. A stainless steel archwire was used at 0°, 3° and 5° angulations. Metal ligatures, conventional elastic ligatures, and low friction elastic ligatures were also tested. A universal testing machine applied friction between brackets and wires, simulating sliding mechanics, to produce 2-mm sliding at 3 mm/minute speed. Results: Two-way analysis of variance demonstrated a significant effect of the interaction between brackets and angulations (p < 0.001). Tukey test indicated that the highest frictional resistance values were observed at 5° angulation for In-Ovation L, PSWb bracket with non conventional ligature, and STb bracket with metal ligature. As for 3D, PSWb with conventional or metal ligatures, and STb brackets with non conventional ligature, showed significantly lower static frictional resistance with 0° angulation. At 0° angulation, STb brackets with metal ties, In-Ovation L brackets and 3D brackets had the lowest frictional resistance. Conclusions: As the angulation increased from 0° to 3°, static friction resistance increased. When angulation increased from 3° to 5°, static friction resistance increased or remained the same. Self-ligating 3D and In-Ovation L brackets, as well as conventional STb brackets, seem to be the best option when sliding mechanics is used to perform lingual orthodontic treatment.

RESUMO Objetivo: avaliar o atrito estático de fios de aço inoxidável em braquetes linguais autoligáveis ativos e passivos, e braquetes linguais ligados convencionalmente, com angulações de segunda ordem. Métodos: dois tipos de braquetes linguais convencionais para caninos (STb light, Ormco, e PSWb, Tecnident) e dois tipos de braquetes autoligáveis, um ativo (In-Ovation L, GAC) e outro passivo (3D, Forestadent), foram avaliados. Um fio de aço inoxidável com angulações de 0°, 3° e 5° foi utilizado. Ligaduras metálicas, elásticas convencionais e ligaduras elásticas de baixo atrito também foram testadas. Uma máquina de ensaio universal causou atrito entre os braquetes e os fios, simulando uma mecânica de deslizamento de 2mm, a uma velocidade de 3mm/minuto. Resultados: a análise de variância de dois níveis demonstrou haver um efeito significativo resultante da interação entre braquetes e angulações (p < 0,001). O teste de Tukey indicou que os valores mais altos de resistência ao atrito foram observados com uma angulação de 5° no braquete In-Ovation L, e no braquete STb com ligadura metálica. Já os braquetes 3D e In-Ovation L, e os braquetes STb com ligadura não convencional apresentaram valores de resistência ao atrito significativamente baixos com uma angulação de 0°. Com angulação de 0°, os braquetes STb com ligaduras metálicas, braquetes In-Ovation L e braquetes 3D apresentaram os mais baixos valores de resistência ao atrito. Conclusões: à medida que a angulação aumentou de 0° para 3°, a resistência ao atrito estático também aumentou. À medida que a angulação aumentou de 3° para 5°, a resistência ao atrito estático também aumentou ou continuou a mesma. Os braquetes autoligáveis 3D e In-Ovation L, assim como os braquetes convencionais STb, parecem ser as melhores opções quando a mecânica de deslizamento é usada no tratamento ortodôntico lingual.